Material | No. | Mode I fracture test | Previous CIE model | Modified CIE model | ||||
---|---|---|---|---|---|---|---|---|
KICT (MPa∙m0.5) | hc (mm) | KICP (MPa∙m0.5) | \(\frac{{K_{{{\text{ICP}}}} - K_{{{\text{ICT}}}} }}{{K_{{{\text{ICT}}}} }}\) (%) | hc (mm) | KICM (MPa∙m0.5) | \(\frac{{K_{{{\text{ICM}}}} - K_{{{\text{ICT}}}} }}{{K_{{{\text{ICT}}}} }}\)(%) | ||
S30408 | 1 | 152.33 | 0.097 | 183.41 | 20.40 | 0.063 | 144.27 | 5.29 |
2 | 0.151 | 231.27 | 51.82 | 0.064 | 147.80 | – 2.97 | ||
SA508-3 | 1 | 171.13 | 0.098 | 231.14 | 35.07 | 0.057 | 175.9 | 2.78 |
2 | 0.101 | 235.45 | 37.58 | 0.051 | 165.18 | − 3.47 | ||
Q345R | 1 | 176.70 | 0. 202 | 248.73 | 40.76 | 0.091 | 165.7 | − 6.23 |
2 | 0. 207 | 261.87 | 48.20 | 0.095 | 167.7 | − 5.09 | ||
18MnMoNbR | 1 | 223.00 | 0.158 | 296.32 | 32.87 | 0.071 | 192.78 | − 13.55 |
2 | 0.178 | 317.52 | 42.38 | 0.064 | 184.37 | − 17.32 |