Table 2 Parameters fitted from EEC

From: Efficient Preparation of Nanoparticle-Reinforced Nickel-based Composite Coating with Highly Preferred (220) Orientation

Preparation

method

TC(220)

(%)

Rs

(Ω·cm2)

CPE1

Rc

(Ω·cm2)

CPE2

Rct

(Ω·cm2)

Y1 (S·cm−2·sn)

n1

Y2 (S·cm−2·sn)

n1

CED (8 A/dm2)

40.7

28.37

8.579×10−4

0.6753

1.476×102

8.759×10−4

0.6846

3.846×103

JED (180 A/dm2)

41.4

25.83

1.661×10−4

0.5643

4.423×103

1.658×10−4

0.5635

1.267×104

JED (190 A/dm2)

63.9

28.32

3.686×10−5

0.8795

1.159×103

4.880×10−5

0.5677

2.119×104

JED (200 A/dm2)

75.6

28.83

2.588×10−5

0.8722

1.571×103

3.386×10−4

0.6184

2.608×104

JED (210 A/dm2)

93.4

24.97

3.543×10−5

0.8938

2.309×103

2.463×10−5

0.7570

3.499×104

JED (220 A/dm2)

97.7

28.04

6.916×10−6

0.8984

7.025×103

1.566×10−5

0.8623

5.989×104