From: Milling Force Model for Aviation Aluminum Alloy: Academic Insight and Perspective Analysis
Ref. | Cutter material | Lubrication | Workpiece | Ktc (N/mm2) | Kte (N·mm) | Krc (N/mm2) | Kre (N·mm) | Kac (N/mm2) | Kae (N·mm) |
---|---|---|---|---|---|---|---|---|---|
[189] | Cemented carbide | Dry | Al6082-T6 | 631 | 13 | 99 | 10 | 273 | 2. 8 |
[190] | Cemented carbide | Dry | Al7075-T6 | 767.01 | 27.7 | 168.8 | 26.6 | 222 | 0.7 |
[160] | Cemented carbide | Dry | Al6061-T6 | 243.77 | 7.53 | 113.5 | 7.83 | ‒ | ‒ |
[160] | Cemented carbide | Dry | Al7075-T6 | 600.46 | 17.9 | 180.96 | 20.42 | ‒ | ‒ |
[150] | Cemented carbide | mql | AlMgSi0.5 | 561.2 | 204.3 | 194.4 | 16.2 | 6.7 | 2.2 |
[157] | Cemented carbide | Dry | Al7050-T7451 | ‒ | 23.4 | ‒ | 35.16 | ‒ | 0 |
[156] | High-speed steel | Dry | Al7075 | 951.365 | 11.115 | 262.597 | 11.314 | 323.33 | 1.105 |
[47] | Cemented carbide | Dry | Al7075 | 1319.41 | 19.65 | 788.83 | 26.77 | 48.75 | 2.05 |