From: Study of Cracking Mechanism and Wear Resistance in Laser Cladding Coating of Ni-based Alloy
Laser power
LP (W)
Scanning speed
SS (mm/s−1)
Powder feeding rate
PFR (g/min−1)
Defocusing
D (mm)
Overlap rate
Η (%)
2100
8
6.6
14
50