Table 1 Compositions of selected positions in Figure 5 for the EBSM Nb-Si based alloy after annealing at 1450 °C for 5 h measured by SEM-EDS (at.%)

From: Morphological Heredity of Intermetallic Nb5Si3 Dendrites in Hypereutectic Nb-Si Based Alloys via Non-Equilibrium Solidification

Position

O

Nb

Si

Ti

Cr

Al

+1

3.35

59.29

2.49

28.50

3.62

2.75

+2

1.77

43.90

31.93

20.49

0.19

1.72

+3

15.90

25.11

10.58

46.92

0.44

1.05