Grinding Characteristics of MoS2-Coated Brazed CBN Grinding Wheels in Dry Grinding of Titanium Alloy

As an important green manufacturing process, dry grinding has problems such as high grinding temperature and insufficient cooling capacity. Aiming at the problems of sticking and burns in dry grinding of titanium alloys, grinding performance evaluation of molybdenum disulfide (MoS2) solid lubricant coated brazed cubic boron carbide (CBN) grinding wheel (MoS2-coated CBN wheel) in dry grinding titanium alloys was carried out. The lubrication mechanism of MoS2 in the grinding process is analyzed, and the MoS2-coated CBN wheel is prepared. The results show that the MoS2 solid lubricant can form a lubricating film on the ground surface and reduce the friction coefficient and grinding force. Within the experimental parameters, normal grinding force decreased by 42.5%, and tangential grinding force decreased by 28.1%. MoS2 lubricant can effectively improve the heat dissipation effect of titanium alloy grinding arc area. Compared with common CBN grinding wheel, MoS2-coated CBN wheel has lower grinding temperature. When the grinding depth reaches 20 μm, the grinding temperature decreased by 30.5%. The wear of CBN grains of grinding wheel were analyzed by mathematical statistical method. MoS2 lubricating coating can essentially decrease the wear of grains, reduce the adhesion of titanium alloy chip, prolong the service life of grinding wheel, and help to enhance the surface quality of workpiece. This research provides high-quality and efficient technical support for titanium alloy grinding.


Introduction
Titanium alloy has significant applications in the aerospace field due to its superior physical and mechanical properties [1][2][3], such as high strength, corrosion resistance, and high temperature resistance.Grinding technology, as the main method of precision processing, has been widely utilized in the processing of titanium alloy aeronautical parts [4][5][6][7].However, due to the special chemical, physical and mechanical properties of titanium alloy, it is easy to appear adhesion and debris defects in grinding, which lead to more grinding heat and serious tool wear.Moreover, titanium alloy has the chemical reactions with cutting fluids and produces the harmful chemicals, which not only posed a threat to the health and environment of operators, but also consumed a large amount of costs in the treatment of cutting fluids, which can no longer meet the green and sustainable development consciousness [8,9].
To solve grinding burn and meet the needs of green processing, scholars have proposed many green processing technologies such as dry cutting, cryogenic machining and minimum quantity lubrication [10][11][12].From the perspective of the environment, compared with cryogenic machining and minimum quantity lubrication, dry grinding has the advantages of reducing energy consumption (such as no pumping and special equipment), and reducing resource waste (filtration device and waste liquid treatment).However, dry grinding is difficult to obtain the better machining quality.Therefore, it is important to improve the grinding condition during dry grinding, reduce the grinding temperature and ensure the grinding quality.The solid lubricant with layered structure was introduced into the grinding contact zone to form a lubricating film on the contact interface, which can minimize the friction at the grinding contact interface and reduce the thermal damage strength to a certain extent [13].Matthew et al. [14] applied the different solid lubricants in grinding and found that the non-toxic solid lubricants can reduce costs, protect the environment, and improve the quality of ground surface.Adhakrishnan et al. [15] studied the comparative test of dry grinding with graphite as lubricant and traditional grinding, and confirmed that graphite assisted dry grinding has better grinding quality, and the grinding force and temperature have been greatly improved.Shaji et al. [16] research shows that when there are sufficient lubrication conditions in the grinding area, the friction coefficient of the ground surface will be reduced.At the same time, the burn of the ground surface can be avoided and the grinding quality can be improved.Rahmati et al. [17] developed a nanolubricant containing MoS 2 nanoparticles for the milling of AL6061-T6 alloy.The rolling action of the nanoparticles at the tool-workpiece interface significantly reduced the cutting forces and effectively improved the surface morphology of the machined workpiece.Ding et al. [18] designed a self-lubricating grinding wheel.The solid powder lubricant is blown out of the grinding wheel cavity to the grinding surface by centrifugal force, thus improving the friction and wear performance of the grinding wheel during grinding.Mahathanabodee et al. [19] added hexagonal boron nitride solid lubricant to 316L stainless steel composites and found that the addition of lubricant can effectively improve the friction properties of materials.Zhao et al. [13] prepared MoS 2 embedded metal composites by liquid phase sintering.The friction properties of different samples of solid lubricants with different concentrations were evaluated.The results showed that MoS 2 samples had better mechanical and tribological properties at the same lubricant concentration.
The above research shows that the grinding quality and friction and wear properties of materials can be effectively improved by introducing solid lubricants.However, there is little research on the influence of solid lubricants on the dry grinding of titanium alloys, and the above research requires the preparation of special lubricant feeding devices or the preparation of mixed abrasive wheels through special processes.The combination of solid lubricant and cubic boron nitride (CBN) orderly arranged grinding wheel by means of coating can not only make use of the advantages of ordered arrangement of CBN grinding wheel and solid lubricant to realize the research of titanium alloy dry grinding process, but also the realization method is simple and easy to operate.Therefore, in this study, MoS 2 is used as the solid lubricant coating material of CBN orderly arrangement grinding wheel (MoS 2 -coated CBN wheel), and the dry grinding tests with MoS 2 -coated CBN wheel in titanium alloy materials were carried out.The lubrication mechanism of MoS 2 solid lubricant in the grinding process is analyzed.The influence of grinding parameters on grinding force, grinding temperature and surface roughness, as well as the characteristics of grain wear in the grinding process are analyzed, which provides technical support for efficient and high-quality grinding of titanium alloy.

Lubrication Mechanism of Solid Lubricating Coating
The lubrication mechanism of solid lubricant is that the solid lubrication phase is coated on the surface of abrasive grains by organic bonding hot coating method, forming a lubrication film between workpiece and abrasive grains.The lubrication layer can improve the grinding environment in the contact zone, inhibit abrasive particle adhesion wear, reduce the temperature, and achieve the purpose of improving the grinding performance of titanium alloy [20].The abrasive grains slip on the surface of the titanium alloy.With the action of load, grains are pressed into the titanium alloy.If the contact area increases, the friction will also increase, and the furrow phenomenon will occur, as shown in Figure 1(a).If the abrasive grains slip directly on the surface of titanium alloy, although the contact area will not increase, due to the temperature rise of the friction surface, occlusion is easy to occur, as shown in Figure 1(b).As shown in Figure 1(c), there is a solid lubricant between the two friction surfaces, and its shear resistance is very small, so the external friction between the two friction surfaces is transformed into the internal friction between the molecules of the solid lubricant.As shown in Figure 1(d), the solid lubrication mechanism of solid lubrication film is a solid lubricant with layered structure, which has sliding characteristics under the action of shear force.
The abrasive grains and the workpiece are separated by solid lubrication coating at the beginning of cutting, and the friction (F f ) generated is only the shearing force (F τ ) generated inside the solid lubricant.At this time, the F f can be expressed as follows: where A r is the actual contact area, which can be obtained from the following formula [21]: where R, E and P are the radius of curvature of the contact arc region, the elastic modulus of the substrate and the load, respectively.At this time, the friction coefficient μ can be expressed as: As the grinding progresses, a lubricating film is formed under the action of pressure and friction, which is in a state of boundary lubrication.The ultimate shear stress of the solid lubricating film is τ cmax , and it is assumed that τ cmax = dτ 0 , τ 0 is the shear strength limit of the MoS 2 solid lubricating film.The premise for the isolation and friction reduction of the MoS 2 solid lubricating film between the grinding wheel and the material surface is as follows [22]: where k is a constant of k >1, σ 0 is the compression yield limit of titanium parts, and σ is the normal compressive stress formed by the normal load.According to the basic theory of adhesive friction, kτ 0 2 =σ 0 2 , the friction coefficient μ can be expressed as follows: (1) (4) It can be concluded that the friction force at this time is a constant value.The lubricant has been coated on the surface of the abrasive, and there is no need for a penetration process.The solid lubricating coating can withstand a lot of pressure.With the reduction of the relative sliding speed of the friction surface of the moving pair and the reduction of the lubricant thickness and surface roughness, the friction surface is too close, so the micro convex contact increases, thus entering the boundary lubrication state.At this time, the tribological properties between the friction surfaces will be determined by the interaction between the lubricant and the surface and the properties of the generated boundary film.Therefore, when there is a layer of MoS 2 lubricating film between the abrasive grains and titanium alloys surface, the friction coefficient μ is reduced.

Test Device and Method
The specific steps for the preparation of MoS 2 -coated CBN wheel used in this study are as follows: Firstly, MoS 2 lubricant powder is passed through a sieve, the lubricant phase powder is selected and baked in oven for two hours.Secondly, the selected binder polyvinyl butyral and the lubricating phase powder are mixed in a certain proportion in a sealed vessel, and placed in an ultrasonic cleaner for ultrasonic vibration for one hour.And then evenly coat it to wheel abrasive grains, then dry it in the natural environment for 24 h.The prepared MoS 2 -coated CBN wheel is shown in Figure 2.
The material properties of Ti-6Al-4V are shown in Table 1, and the sample size of the workpiece is 60×10×50 mm, ground surface size: 50×10 mm.The test was carried out on the DMG machining center (ULTRASONIC 20 linear, spindle speed range: 40000 r/ min), and the test device is shown in Figure 3. Before the grinding test, all grinding wheels need to be reshaped and sharpened, so that the grinding wheels are in the same state before grinding.In this paper, a single-layer brazed CBN wheel (common CBN wheel) and MoS 2 -coated CBN wheel are used to carry out dry grinding tests on titanium alloy materials.The CBN grains on the wheel are arranged in an orderly manner.Table 2 shows the wheel parameters and grinding parameters.And the grinding temperature and grinding force during grinding were measured by artificial thermocouple and 9129A dynamometer.Use the roughness meter to detect the roughness value on the machine, measure three different positions, and calculate the average value as the final result of each group of tests.Three-dimensional video and SEM were used to extract the surface morphology, abrasive grain height and distribution characteristics of the grinding wheel after each group of tests, and analyze the grinding wheel wear degree.

Grinding Force
The grinding process can be divided into three stages of rubbing, ploughing and cutting [23].Through the extrusion of the abrasive grains on the metal material, the metal layer produces elastic-plastic deformation and shear slip.When the strain of the material in the grinding area reaches a certain value, the material peels off the workpiece in the form of debris.As shown in Figure 4, the grinding force can be decomposed into the cutting force on the abrasive rake face and the sliding friction force on the blunt face in the contact area.If the contact mode of the abrasive contact area is regarded as the form of sliding friction, the grinding force is decomposed according to the tangential and normal directions [24]: where F t , F tc and F ts are tangential grinding force, tangential grinding force generated in cutting action and sliding friction tangential grinding force respectively.F n , F nc and F ns are normal grinding force, normal grinding force generated in cutting action and normal grinding force caused by sliding action respectively.γ, F x , F y , F x ′ and F y ′ are the absolute values of the rake angle of the abrasive grains, the positive pressure in the normal direction of the grain contact surface, the sliding friction in the tangent direction of the grain contact surface, the positive pressure on the wear plane and the sliding friction along the tangent direction of the wear plane, respectively.Therefore, the relationship between F t , F n and sliding friction coefficient μ is as follows: (6)   Assuming that the pressure per unit area among the grain and the contact material is F p , the contact area among the grain and the contact material is S c , the pressure per unit area at the abrasive wear plane is F p ′, and the surface of impact among the grain and the machined surface is S ls , the following relationship can be obtained: It can be seen from the analysis in Section 2.1 that the sliding friction coefficient of the MoS 2 -coated CBN wheel is smaller than that of the common CBN wheel.Because of the existence of the lubricating layer, the contact area S c between the grains and the contact surface decreases.Therefore, the following relationship exists: The variation of grinding force with grinding parameters is shown in Figure 5.With the increase of cutting depth a p , the normal force F n and tangential force F t of both MoS 2 -coated CBN wheel and common CBN wheel increase significantly (Figure 5(a)).The reason is that when the grinding wheel speed v s and workpiece speed v w are constant, increasing the cutting depth a p , the depth of grain cutting into the material increases, and the maximum undeformed thickness h max increases.Moreover, the pressure F p per unit area among abrasive grains and grinding arc area increases, the contact area S c among grains and grinding area increases, and the F n increases.Similarly, the F t also shows an increasing trend.At the same time, the geometric contact arc length among the wheel and the workpiece also increases, and the dynamic effective grains involved in grinding increase, so the grinding force increases.During grinding, the feed speed v w increases and the grinding force gradually increases (Figure 5(b)).With the increase of v w , the contact area between grains and workpiece increases in unit time, and the cutting area of abrasive grains on materials increases, and the removal volume increases.When the grinding depth is certain, the pressure F p per unit area among grains and grinding arc area remains unchanged, the contact area S c among grains and grinding arc area increases, and the F n increases.Similarly, the F t also shows an (8) Figure 5 Influence of grinding parameters on grinding force increasing trend.The grinding force under different wheel speeds v s is shown in Figure 5(c).the wheel speeds v s increases and the grinding force gradually increases.when v s is from 5 m/s to 15 m/s, the force in grinding of these two types of grinding wheels is greatly reduced, and when v s is from 15 m/s to 20 m/s, the force in grinding of these two types of grinding wheels is slowly decrease.With the increase of v s , the time of a single abrasive grain in the grinding arc area decreases.And, more abrasive grains participate in grinding, reducing the wear of the abrasive blade, and intensifying the "sliding friction" effect on the workpiece material.Therefore, the force in grinding shows a slow downward trend.
From Figure 5, it is known that the force in grinding of MoS 2 -coated CBN wheel is lower than that of common CBN wheel under the same conditions.It is known from the above analysis that the sliding friction coefficient μ MoS2 of the MoS 2 -coated CBN wheel is smaller than the sliding friction coefficient μ wt of the common CBN wheel, which reduces the friction of grain cutting materials.On the other hand, due to the lubricating effect of MoS 2 , the wear behavior of the abrasive grains during the grinding process is weakened, and the grinding edge is relatively sharp.When v s = 20 m/s, v w = 2400 m/min, a p = 10 μm, the normal grinding force F n is reduced by 42.5% at the maximum, and the tangential grinding force F t at this time is reduced by 28.1%.

Grinding Temperature
The energy predominantly exists as grinding heat during the grinding process, and minor grinding heat will disperse with the chips, and most of them accumulates in the grinding arc area [25][26][27].The grinding temperature at the contact point between the grains and the workpiece is the highest, which is also the heat source of the grinding process.Grinding temperature is an intuitive manifestation of the effect of abrasive grains on material removal in the grinding of Ti-6Al-4V materials.Therefore, this paper analyzes the influence law between grinding temperature and grinding parameters.Semi-artificial thermocouple device is used to collect the temperature generated in grinding (Figure 3), and use standard thermocouple to calibrate the corresponding relationship between potential U and temperature T in Ti-6Al-4V and constantan wire system.The calibration function is as follows [28]: Figure 6 shows the comparison of the influence trend of grinding parameters of two kinds of wheels on grinding temperature.The relationship between grinding depth a p and grinding temperature shows the trend in Figure 6(a).In the process of increasing a p from 5 μm to 20 μm,  the grinding temperature of MoS 2 -coated CBN wheel increased from 103.3 ℃ to 213.7 ℃, increased by 106.9%, and the grinding temperature of common CBN grinding wheel increased from 106.7 ℃ to 278 ℃, increased by 160.5%, showing a sharp upward trend, but no burns occurred within the test parameters.With the increase of a p , the friction force and cutting depth of grains on the workpiece surface increase, and the material removal thickness increases, and the capacity consumed in the processing process increases, therefore, the grinding specific energy increases and the temperature increases.The grinding temperature increases gradually with the increase of the feed rate v w , as shown in Figure 6(b).The increase of v w will speed up the movement of the grinding heat source, but the contact area among the grains and the workpiece material adds in per unit time, then the cutting area of grains on the material rises, and cutting thickness and grinding temperature rises.Under the comprehensive effect that the heat generation effect is greater than the heat dissipation effect, the grinding temperature shows an upward trend.The relationship between grinding speed v s and grinding temperature shows the trend in Figure 6(c).With the increase of v s , the time for grains to act on the grinding arc area decreases.In a certain period of time, more abrasive grains participate in grinding, resulting in the intensification of the "sliding friction" effect of abrasive grains on the workpiece material.Therefore, more energy is converted into grinding heat in the grinding arc area.
According to the analysis of grinding temperature, the grinding temperature is at a low level within the range of parameter selection (Figure 6).Brazed CBN grinding wheel abrasive grains are arranged in an orderly manner to optimize the landform, high abrasive exposure, large chip holding space, and the grinding wheel is not easy to be blocked.MoS 2 -coated CBN wheel adds MoS 2 lubricant on the basis of brazing CBN grinding wheel, which provides a carrier for heat flow, reduces friction heat energy and reduces grinding temperature.When v s = 20 m/s, v w = 2000 mm/min and a p = 20 μm, the grinding temperature decreases by 30.5%.Moreover, due to the orderly arrangement of the abrasive grains of the brazed grinding wheel, the large chip holding space between the abrasive grains is full of lubricant.After the lubricant on the surface of the abrasive grains are worn, the lubricant between the abrasive grains play a complementary role and prolongs the service life of the lubricating coating.

Grinding Wheel Grain Wear
Due to the characteristics of the grinding wheel, grains wear is inevitable during the entire grinding process.Severe grinding wheel wear affects the geometric accuracy and surface quality of the workpiece [29,30], Therefore, the study of grain wear is an important means to evaluate the performance of grinding wheel.
As the material removal volume V w increases, the grain wear morphologies of the two grinding wheels are shown in Figure 7.When V w reaches 400 mm 3 , the cutting edges of the two types of grinding wheel grains have different degrees of wear.When V w increased from 400 mm 3 to 800 mm 3 , the grains of both grinding wheels were slightly broken, but no grains fell off, and no obvious chips adhered to the grinding wheel.At this time, the grain micro damage of common CBN wheel was relatively serious.When the V w increased from 800 mm 3 to 1200 mm 3 , the grains of the two grinding wheels were broken in large pieces, and the common CBN wheel grains have obvious titanium alloy chip adhesion.From the microstructure around the grain of the MoS 2 -coated CBN wheel, it can be seen that there is good infiltration between the lubricant and CBN grains, and there is no chip adhesion.
The mathematical statistics method is used to analyze the wear of the grinding wheel grains.According to the change of grinding wheel grain wear state with the amount of material removed, the wear types (no wear, abrasion wear, micro-fracture, macro-fracture) and distribution rules of CBN grains are counted, the height difference between the exposed height of grains and the grinding wheel matrix is measured and calculated, and the grinding wheel grain wear is quantified, as shown in Figure 8. Gaussian distribution probability density function is adopted as follows [31,32]: where h, μ and σ represent the contour height of grain relative to matrix, the mean value of contour height and the standard deviation of contour height, respectively.
The protruding height and wear morphology of CBN grains on the surface of the grinding wheel were measured by a three-dimensional video microscope, each group randomly collects 60 grain data as the basis.The Gaussian distribution of the grain bulge height is shown in Figure 9, and the wear type distribution of CBN grains is shown in Figure 10.By analyzing the mean probability density of the initial protruding height of CBN grains, the average protruding height of MoS 2 -coated CBN wheel abrasive grains is 291.53 μm, and the average protruding height of common CBN wheel abrasive grains is 351.08 μm.This is because the MoS 2 -coated CBN wheel grains are arranged in an orderly manner, the large chip space between the abrasive grains is filled with lubricant, and the height difference from the highest point of grain and the matrix is reduced.(15)   The type and distribution of grinding wheel grain wear are shown in Figure 10. Figure 10(a) shows the variation law of abrasive wear type of common CBN grinding wheel with V w .With V w increasing to 400 mm 3 , the CBN grains that did not participate in grinding accounted for about 31.7%, the CBN grains with micro-fracture and macro-fracture increased slowly from 13.3% and 6.7% to 20% and 11.7%, respectively, and the CBN grains with abrasion wear decreased from 41.7% to 36.7%.When V w continued to increase to 1200 mm 3 , the proportion of CBN grains that did not participate in grinding rapidly to about 3.3%, while the CBN grains with micro-fracture and macro-fracture rapidly increased to 36.7% and 46.7%, and the CBN grains with abrasion wear continued to decrease to about 13.3%.The grain wear type and distribution law of MoS 2 -coated CBN wheel are shown in Figure 10(b).It can be seen that as V w increases to 400 mm 3 , about 30% of CBN grains did not participate in grinding, the CBN grains with micro-fracture and macro-fracture slowly increase from 16.7% and 3.3% to 18.3% and 6.7%, respectively, and the CBN grains with abrasion wear increase from 36.7% to 45%.When V w continued to increase to 1200 mm 3 , the proportion of CBN grains that did not participate in grinding rapidly decreased to about 5%, while the CBN grains with micro-fracture and macro-fracture rapidly increased to 38.3% and 36.7%, and the CBN grains with abrasion wear continued to decrease to about 18.3%.This indicates that with the increase of material removal volume, some CBN grains with higher exposed heights take part in grinding first, and wear and tear, micro-fragmentation and even big fragmentation occur under heavy load.Most of CBN grains with lower exposed heights also take part in material removal gradually with the fragmentation of surrounding grains.Comparing the two grinding wheels, it is found that MoS 2 lubricant can effectively reduce the wear of the grinding wheels and prolong the service life of the grinding wheels.

Ground Surface Quality
Figure 11 shows the influence of grinding parameters on the surface roughness of titanium alloy ground with MoS 2 -coated CBN wheel and common CBN wheel.To reduce the measurement error, three measurement points are accumulated under each group of grinding parameters to obtain the mean value.When the grinding depth a p changes from 5 μm increased to 20 μm.The surface roughness of the workpiece increases significantly (Figure 11(a)).The increase of a p and the increase of the depth of grain ploughing into the workpiece lead to the longer stroke of abrasive grains contacting the workpiece material.Therefore, there are deep cutting marks on the surface of the workpiece, and the roughness increases.The effect of different feed speeds v w on the surface roughness is shown in Figure 11(b).When the feed speeds v w changes from 800 mm/min to 2400 mm/min, the surface roughness of the workpiece first increases, Figure 11 Influence of grinding parameters on ground surface roughness then decreases and then increases.The main reason is that due to the increase of v w , the cutting thickness of single abrasive grains also increases, the grinding force increases and the roughness increases.Under the action of tangential force, the cutting edges of some highly exposed abrasive grains are worn and broken, forming multi-edge cutting.And the low exposure abrasive grains participate in the material removal, and the roughness is improved [33].At this time, it is beneficial to reduce the surface roughness by selecting a lower speed of the workpiece for grinding the surface.When the grinding speed v s changes from 5 m/s raised to 20 m/s.The surface roughness of the workpiece reduction significantly (Figure 11(c)).Therefore, higher wheel speed can be selected to reduce grinding roughness.When the grinding wheel speed is too low, the cutting thickness of a single abrasive particle is large, which not only increases the surface roughness of the workpiece, but also increases the abrasive wear of the CBN grinding wheel.
The surface roughness of MoS 2 -coated CBN wheel grinding is lower than that of common CBN wheel grinding titanium alloy.Because the lubricant exerts its effective lubricating effect in the grinding zone by forming a lubricating film on the grain surface.In the absence of solid lubricants, the surface of the grains is in direct contact with the wear debris, and the friction is relatively large.In the case of high temperature and high pressure, residues are formed, which stick to the surface of the workpiece or the grinding wheel, and even block and passivate the grinding wheel, therefore, a smaller surface roughness value cannot be obtained.Figure 12 shows the surface topography of the workpiece after grinding with two grinding wheels.It can be seen that there are a lot of built-up edge and grinding bond on the surface of titanium alloy with common CBN wheel.Due to the effective lubricating effect of MoS 2 lubricant, the ground surface morphology of MoS 2 -coated CBN wheel has been greatly improved, and it is also more conducive to prolong the service life of grinding wheel.

Conclusions
(1) The MoS 2 -coated CBN wheel enters the grinding state, and a layer of MoS 2 solid lubricating film exists between the workpiece surface and abrasive grains, the friction coefficient between the grain and the workpiece surface is diminished, consequently reducing the grinding force.(2) Both the grinding force of MoS 2 -coated CBN wheel and common CBN grinding wheel increase with the increase of grinding depth and feed speed, and decrease with the increase of wheel linear speed.Among them, the grinding depth has the greatest impact on the grinding force, and the grinding force of MoS 2 -coated CBN wheel is significantly lower than that of common CBN grinding wheel.Within the range of parameter selection, the normal grinding force F n decreases by 42.5%, and the tangential grinding force F t decreases by 28.1%.(3) The grinding depth has the most significant effect on the grinding temperature.When the grinding depth increased from 5 μm to 20 μm, the grinding temperature of MoS 2 -coated CBN wheel increased by 106.9%, while the grinding temperature of common CBN grinding wheel increased by 160.5%, and showed a sharp upward trend.There was no burn on the ground surface of the workpiece within the test parameters.MoS 2 lubricant provides a carrier for heat flow, reduces frictional heat energy and reduces grinding temperature.(4) The wear of CBN grains of grinding wheel is analyzed through mathematical statistics method, and the wear of grains is quantified.The analysis shows that MoS 2 lubricant can essentially reduce the wear of CBN grains and prolong the service life of grinding wheel.

Figure 1
Figure 1 Friction and wear model of abrasive grains in solid lubricating coating: (a) Cut into workpiece, (b) Slip on workpiece surface, (c) Solid lubricated grain cut into workpiece and (d) solid lubrication mechanism

Figure 2
Figure 2 Single layer brazed CBN grinding wheel with MoS 2 coated

Figure 4
Figure 4 Composition of grinding force

Figure 6
Figure 6 Influence of grinding parameters on grinding temperature

Figure 7 Figure 8
Figure 7 Evolution of abrasive wear morphology of two CBN grinding wheels (V w =400-1200 mm 3 )

Figure 9 (
Figure 9(a, b) respectively show the height profile histograms of the grains of MoS 2 -coated CBN wheel and common CBN wheel when the material removal amount reaches 400 mm 3 .Due to the limited number of CBN grains collected, the standard deviation of the figure obtained is large.Figure 9(c) shows the trend of the average grain height distribution with the material removal volume.When the V w reaches 400 mm 3 , the average protruding height of grains of MoS 2 -coated CBN wheel is 273.91 μm, the average protruding height of grains of common CBN wheel is 302.79 μm, and the wear height of the common CBN wheel is obviously larger.When the V w reaches 1200 mm 3 , the average protruding height of MoS 2 -coated CBN wheel abrasive grains is 227.39 μm, and the average protruding height of abrasive grains of common CBN wheel is 234.82 μm.It can be seen that MoS 2 lubricant can effectively slow down the wear of grinding wheel grains.The type and distribution of grinding wheel grain wear are shown in Figure10.Figure10(a)shows the variation law of abrasive wear type of common CBN grinding wheel with V w .With V w increasing to 400 mm 3 , the CBN

Figure 9 Figure 10
Figure 9 Gaussian distribution diagram of grain bulge height and statistical diagram of average contour height

Figure 12
Figure 12 Comparison of ground surface morphology of two kinds of grinding wheels: (a) MoS 2 -coated CBN wheel grinding and (b) common CBN wheel grinding

Table 2
Experimental parameters