From: Hot Extrusion Processing of Al–Li Alloy Profiles and Related Issues: A Review
Alloy | Temper | Profile and testing positions | Testing orientation | E (GPa) | Strength (MPa) | EL (%) | Ref. | Ref. for DMP | ||
---|---|---|---|---|---|---|---|---|---|---|
TY | UTS | CY | ||||||||
1420 | ‒ |
| L | 76.4 | 312 | 432 | ‒ | 10.2 | [21] | [21] |
2090 | T6 |
| L | ‒ | ~ 750 | ‒ | ‒ | ‒ | [22] | |
| L | ‒ | ~ 630 | ‒ | ‒ | ‒ | ||||
8090 | T6 |
| L | ‒ | ~ 550 | ‒ | ‒ | ‒ | [22] | |
| L | ‒ | ~ 440 | ~ 515 | ‒ | ‒ | [25] | |||
| L | ‒ | ~ 420 | ~ 500 | ‒ | ‒ | ||||
8091 | T6 |
| L | ‒ | ~ 630 | - | ‒ | ‒ | [22] | |
| L | ‒ | ~ 495 | ~ 555 | ‒ | ‒ | [25] | |||
| L | ‒ | ~ 440 | ~ 510 | ‒ | ‒ | ||||
2099 | T83 |
| L | ‒ | ~ 600 | ~ 630 | 622 | ‒ | ||
45o | ‒ | ~ 475 | ~ 425 | 472 | ‒ | |||||
T | ‒ | ~ 445 | ~ 505 | 435 | ‒ | |||||
| L | ‒ | ~ 475 | ~ 535 | 483 | ‒ | ||||
45o | ‒ | ~ 425 | ~ 480 | 393 | ‒ | |||||
T | ‒ | ~ 455 | ~ 505 | 520 | ‒ | |||||
| L | ‒ | ~ 590 | ~ 600 | 561 | ‒ | ||||
45o | ‒ | ~ 445 | ~ 485 | 397 | ‒ | |||||
T | ‒ | ~ 490 | ~ 525 | 445 | ‒ | |||||
2196 | T8511 |
| L | 73.17 | 519.93 | 592.23 | ‒ | 6.97 | [30] | |
| L | 79.85 | 526.97 | 602.08 | ‒ | 7.35 | ||||
2195 | T83 |
| L | ‒ | ~ 620 | ~ 645 | ‒ | ~ 10.5 | [31] | |
45o | ‒ | ~ 500 | ~ 540 | ‒ | ~ 9 | |||||
T | ‒ | ~ 520 | ~ 560 | ‒ | ~ 8 | |||||
| L | ‒ | ~ 580 | ~ 600 | ‒ | ~ 11 | ||||
45o | ‒ | ~ 505 | ~ 555 | ‒ | ~ 16 | |||||
T | ‒ | ~ 590 | ~ 640 | ‒ | ~ 13 |