From: Experimental Study on the Reduction Effect of Pit Texture on Disassembly Damage for Interference Fit
No. | Parameter scheme | Q | No. | Parameter scheme | Q |
---|---|---|---|---|---|
1 | A1B1C1 | 0.63 | 14 | A3B4C1 | 0.54 |
2 | A1B2C2 | 0.48 | 15 | A3B5C2 | 0.25 |
3 | A1B3C3 | 0.52 | 16 | A4B1C4 | 0.61 |
4 | A1B4C4 | 0.45 | 17 | A4B2C5 | 0.78 |
5 | A1B5C5 | 0.60 | 18 | A4B3C1 | 0.76 |
6 | A2B1C2 | 0.34 | 19 | A4B4C2 | 0.44 |
7 | A2B2C3 | 0.36 | 20 | A4B5C3 | 0.58 |
8 | A2B3C4 | 0.28 | 21 | A5B1C5 | 1.13 |
9 | A2B4C5 | 0.55 | 22 | A5B2C1 | 1.43 |
10 | A2B5C1 | 0.45 | 23 | A5B3C2 | 0.65 |
11 | A3B1C3 | 0.46 | 24 | A5B4C3 | 0.82 |
12 | A3B2C4 | 0.30 | 25 | A5B5C4 | 0.73 |
13 | A3B3C5 | 0.58 |
Factor A | Factor B | Factor C | |
---|---|---|---|
\(\overline{{K_{1} }}\) | 0.54 | 0.63 | 0.76 |
\(\overline{{K_{2} }}\) | 0.40 | 0.67 | 0.43 |
\(\overline{{K_{3} }}\) | 0.42 | 0.56 | 0.55 |
\(\overline{{K_{4} }}\) | 0.63 | 0.56 | 0.47 |
\(\overline{{K_{5} }}\) | 0.95 | 0.52 | 0.73 |
R | 0.55 | 0.15 | 0.33 |
Factor influence order | A>C>B | ||
Excellent scheme | A2B5C2 |